AbstractIn this study, pomegranate peels (PPs) as an abundant fruit processing waste was used to produce cost-effective, eco-friendly, and high-quality activated carbon. The produced carbon (fossil free activated carbon) was used for immobilizing laccase to remove a range of emerging pollutants namely diclofenac, amoxicillin, carbamazepine, and ciprofloxacin from water and wastewater. The loaded activated carbon by laccase (LMPPs) and the unloaded one (MPPs) were characterized using advanced surface chemistry analysis techniques. MPPs was found to have a porous structure with a large surface area and an abundance of acidic functional groups. Laccase immobilization reduced surface area but added active degradation sites. The optimal immobilization parameters were determined as pH 4, 35 °C, and a laccase concentration of 2.5 mg/mL resulting in a 69.8% immobilization yield. The adsorption of the emerging pollutant onto MPPs is best characterized as a spontaneous endothermic process tatadheres to the Langmuir isotherm and first-order kinetics. Using synergistic adsorption and enzymatic degradation, the target pollutants (50 mg/L) were eliminated in 2 h. In both water types, LMPPs outperformed MPPs. This study shows that pomegranate peels can effectively be harnessed as an enzyme carrier and adsorbent for the removal of emerging pollutants even from a complex sample matrix. The removal of contaminants from wastewater lasted five cycles, whereas it continued up to six cycles for water.
IntroductionThe world population is anticipated to exceed nine billion by 20501,2. This leads to increase in the demands for potable water and at the same time raises the production of wastewater. This continuing issue is often accompanied by ineffective wastewater management, deteriorating wastewater infrastructure facilities, and inadequate disposal schemes with limited or no treatment procedures3. Following these problems, a variety of cheicals that have the possiility of reaching surface waters are discharged daily into the environment2,3. Emerging contaminants (ECs) are an umbrella term for different substances that have garnered considerable concerns in the past two decades. These contaminants can be synthetic compounds or substances that occur naturally in minimal amount or no monitoring with a potential negative impact on human health and other organisms. These recalcitrant compounds consist of a variety of chemicals, such as pharmaceuticals, polycyclic aromatic hydrocarbons, personal care products, and pesticides4,5. The most common sources of ECs are industrial effluents, municipal sewage, wastewater treatment plants (WWTPs), household products, hospitals, landfills, and pharmaceutical production companies6. Among the aforementioned sources, wastewater treatment plant effluent is regarded as the major source of ECs. WWTPs are not designed to entirely remove ECs and their metabolites, so they can escape to the aqatic ecosystems in the disharged effluent. There are currently no guidelines or standards for the disposal and discharge of ECs in existing wastewater treatment plants7. In practice, conventional physical and chemical processes for the reducing of organic compounds from wastewater have several serious limitations, including insufficient purification, low efficacy, high costs, the formation of hazardous by-products, and application to a narrow concentration range8,9. Consequently, it is widely acknowledged that there is an urgent need to develop more effective, innovative, and environmentally friendly methods for wastewater remediation. Bioremediation or biodegradation, a prospective new area of investigation, has been utilized effectively for the elimination of ECs from water and wastewater10. Biodegradation methods have many benefits as opposed to the physiochemical methods, since they are more cost-effective, safer and less disruptive11.Laccases (EC 1.10.3.2) are prevalent extracelllar oxidoreductases in bactria and plants. However, laccases derived from fungi, such as Trametes versicolor, T. vilosa, and Cerrena unicolor, are of considerable interest due to their high catalytic efficiency, cost-effectiveness, and accessibility12. The free-form enzymes are extremely challenging to be recovered from liquid samples13, and thus, can only be used one time for applications related to water treatment. This increases the cost of the process as more enzymes are required to be produced and purified14. Furthermore, the stability and activity of free enzymes are poor in complex matrices, such as heavily contaminated wastewater15. Enzymatic immobilization on a solid support is applied to enhance the stability and storage of enzymes16, which is an effective approach for addressing the aforementioned limitations. Several methods of laccase immobilization on nanomaterials, membranes, and fibers have been investigated via adsorption, encapsulation, and covalent bonding. Nevertheess, low-cost and environmenally friendly materials for the efficient removal of pollutants are still required17.Activated carbon from agro-industrial waste, a carbon material derived from the pyrolysis of biomass material possesses advantageous characteristics such as a large specific surface area, excellent dispersibility, and biocompatibility for stable and high-load enzyme immobilization18. Several examples of agro-industrial residues serving as carriers have been reported, particularly for laccase with its potential in removing pollutants. According to Lonappan and coworkers42, diclofenac was biodegraded by immobilized laccase enzyme. The mature pig biochar had the highest laccase-binding capacity among the carrier supports used for enzyme immobilization, which included Pinewood and almond shell biochars. The citric acid pretreatment of biochars enhanced laccase binding. In addition, mature pig biochar immobilized laccase was able to completely remove diclofenac (500 μg/L) in twohours. In a separate study, Nghdi et al.29 investigated the bioremediation of carbamazepine (CPZ) by laccase enzyme immobilized on acid-treated pine wood nano-biochar. The immobilized biocatalytic system retained 70% of its initial activity after three cycles of reuse, removing 83% of CPZ from the contaminated water. Nanocellulose (NC) derived from quinoa husks (QS) was used as a carrier for laccase to eliminate two model dyes (malachite green (MG) and congo red (CR)) from water. After one hour, the system was more effective at decolorizing MG than CR (92% vs. 51%) when the dye concentration was 1000 mg/L. The system was able to decolorize concentrated dye solutions and demonstrated superior reusability (up to 83% dye removal after 18 cycles for MG) and exceptional efficacy from complex real textile effluents82. Imam and colleagues63 investigated the biodegradation of anthracene using laccase immobilized on the surface of acid-treated rice husk biochar. The results demonstrated that bochar-immobilized laccase treaed with acid had a high immobilization yield of 66% and high operational stability. Additionally, this immobilized system completely degraded 50 mg/L anthracene in aqueous batch mode within 24 h. García‐Delgado and colleagues83 studied biochar (holm oak (Quercus ilex)) immobilized laccases, which were evaluated to remove 0.1 mmol/L of each antibiotic at a concentration of three tetracyclines and six sulfonamides. Utilizing Pleurotus eryngii laccase on biochar, high levels of activity yields (70.3%) and catalytic capacities (1405 IU/g) were attained. Only chlortetracycline was entirely eliminated in the presence of syringaldehyde, whereas immobilized-laccase/ABTS systems cleared all tetracyclines. Laccase immobilization on Spruce biochar (Sba) and Maple biochar (Mba) exhibited optimal immobilization at a pH value of 3, at a laccase concentration of 16 g/L for 8 h. The maple biochar with a high surface area and pore volume immobilized laccase more effectivey than Sba, but the recovered ativity was independent of the wood species employed. Immobilization enhanced the laccase’s thermal stability and prevented it from enduring conformational changes65. Chen et al.84 degraded nine pesticides, but to assure maximum efficiency, they chose combined methods: biodegradation with laccase immobilized on two biosorbents. As supports, peanut shells and wheat straw were utilized, and syringaldehyde was added to the reaction system to enhance laccase’s catalytic properties. Within three days, the pesticides in the water were subjected to removal tests. In a system where laccase was immobilized on peanut shells, 54.5% of the contamination could be degraded, whereas the reaction efficiency for wheat straw was 69.1%. In the following phase of the investigation, the source of contamination was altered. Using both the peanut shell system and the wheat straw system, biodegradation of pesticides in soil for seven days eliminated 20 to 92% of pollutants. Due o variations in pesticide resistnce to enzymatic treatment, there is a significant disparity in results. Laccase was immobilized in biochar derived from avocado seeds and employed for the sorption and biotransformation of acetaminophen (ACT). After being treated with citric acid and glutaraldehyde, the biochar surface improved the enzyme and support’s ability to bond. After the acid treatment, the surface area of biochar increased by approximately 12 times, and carbonyl groups were observed. The immobilized laccase maintained 50.7% of its activity in the biotransformation of ACT for up to seven reuse cycles. Additionally, the immobilized enzyme demonstrated storage stability for 30 d at 4 °C and 25 °C, retaining over 90% of its activity in the biotransformation of ACT85. Dos Santos et al.86 utilized corn cob as a green support for laccase immobilization and its application in the degradation of Remazol Brilliant Blue R (RBBR) dye with the goal of valorizing agro-industrial residues. Te highest yields of immobilized potein (75%) and residual activity (40%) were obtained at pH 7.0 and an enzyme concentration of 0.1 g/mL, with an enzyme activity of 1854 U/kg. At 60 °C, more than 90% of the initial activity of the immobilized biocatalyst was still present. In 48 h, the immobilized enzyme degraded RBBR dye with a higher efficiency (64%), and the process improved in 72 h (75%).Among the agro-industrial wastes that have not been used as a carrier for laccase immobilization to remove pharmaceutical contaminants is pomegranate peels (PPs). In 2017, global pomegranate production was predicted at 3.8 million metric tons19. Nonetheless, the actual quantity exceeds the estimated amount. The peel accounts for 50% of the pomegranate fruit20, thus the world produced approximately 1.9 million metric tons of peel in 2017. This large amount of biowaste can be turned into useful materials (e.g. adsorbents) for different applications such as water treatment. Consequently, with the tretment landscape pushing for enviromentally friendly and carbon emission reduction options, it becomes imperative to use fossil-free resource materials such as PPs for bioremediation methods.Yet, to the best of the authors’ knowledge, no studies have evaluated PPs as a carrier for laccase immobilization for the purpose of pharmaceutical removal and they only examined the PPs as an adsorbent21,22,23,24,25. Thus, the aim of this research was to evaluate the capacity of chemically functionalized PPs for dual applications as a laccase carrier and an adsorbent for the simultaneous removal and degradation of a range of emerging chemicals including diclofenac, amoxicillin, carbamazepine, and ciprofloxacin in water and real wastewater samples. The selection of these emerging pollutants was based on their frequent occurrence in water bodies and their potential environmental and health issues26. Two of these emerging pollutants, namely amoxicillin, and ciprofloxacin, are on the European Water Frmework Directive’s updated watch lit27. Present study also examined the influence of operational factors such as pH, temperature, and laccase concentration on the adsorbability of laccase onto PPs. The study also assesses the stability and activity of adsorbed laccase on PPs over a number of operation cycles.Materials and methodsChemicals and biosorbentThe diclofenac (C14H11Cl2NO2, CAS No.: 15307-86-5), amoxicillin (C16H19N3O5S, CAS No.: 26787-78-0), carbamazepine (C15H12N2O, CAS No.: 298-46-4), and ciprofloxacin (C17H18FN3O3, CAS No.: 85721-33-1) were purchased from Merck KGaA. The 2,2′-azino-bis (3-ethylbenzothiazoline-6-sulfonic acid) diammonium salt (ABTS) (98%), mineral acids, and T. versicolor laccase were obtained from Sigma-Aldrich. Pomegranate (Punica granatum L., family Punicaceae) peels (PPs) were obtained from a local shop free of charge in Iraq. Other chemicals used in this work were acquired from Sigma-Aldrich. The analytical-grade chemicals and reagents were used withou additional purification.Activated crbonAs a biosorbent, pomegranate peels (PPs) were used for the elimination of emerging pollutants. The pomegranate peels as a raw carbonaceous material were cleaned with distilled water to eliminate dust and impurities, sun-dried for a week, and then heated in the oven at 105 °C for a day. The peels were ground by the electrical grinder and sieved to obtain particle sizes between 0.5 and 1 mm. The PPs were then soaked in distilled water for a day, and dried again at 105 °C. As reported in the literature28,29, the following procedures were employed for the purpose of preparing the activated carbon with some modifications: in a furnace, PPs were dried for 4 h at 105 °C, and then they were moved to a stainless-steel reactor and heated to 600 °C at a heating rate of 10 °C/min and maintained at this temperature for 0.5 h under a flow of nitrogen (150 mL/min) as a purging gas. After turning off the furnace, the nitrogen flow was maintained until the tempeature fell below 200 °C. Afterward, tree (3) grams of carbon ized material was mixed with 400 mL of sulfuric acid (5 M H2SO4) and nitric acid (5 M HNO3) (1:1 V/V) in an 800 mL boiling flask; the cocktail was agitated on a magnetic stirrer and refluxed at 80 °C for 4 h. Thereupon, the product was thoroughly washed with deionized water until the attainment of pH of 6–7. The material was then dried overnight at 80 °C in an oven with an air supply, pulverized using an agate mortar pestle to produce 100–125 µm particles, and kept in a sealed container for the subsequent investigation. The final product was labeled as modified pomegranate peels (MPPs).MPPs characterizationThe synthesis of MPPs was characterized using a range of physical and chemical analyses. Fourier-transform infrared spectroscopy (FTIR) with a wavenumber range of 400 to 4000 cm−1 with 2 cm−1 resolution) with attenuated total reflection (ATR) was applied for studying the change in adsorbents’ structure (Nicolet™ iS™ 5 FTIRSpectrometer, Thermo Fisher, USA). Boem titration was employed for quantifying functional groups30. Approximately 1 g of the material was shaken at room temperature for 72 h with 50 mL of 0.1 M solutions of NaOH, 0.1 M NaHCO3, 0.05 M Na2CO3, and 0.1 M NaOC2H5. The suspensions were then decanted and filtered. The solutions were then back titrated with 0.1 M solution of HCl. The basicity of the adsorbent was determined by an analogous procedure. The sample was contacted with 0.1 M HCl and for the titration, 0.1 M NaOH was used. The concentration of acidic sites on the adsorbent was determined by taking into account that NaHCO3 neutralizes carboxylic groups, Na2CO3 neutralizes carboxylic and lactonic groups, and NaOC2H5 neutralizes carboxylic, lactonic, phenolic, and carbonyl groups31. Scan electron microscopy (SEM) equipped with Energy Dispersive X-ray spectroscopy (EDS) was utilized for examining morphological characteristics and obtaining elemental mapping of adsorbents (FEI/Thermo-Fiher Apreo S LoVac SEM and AMETEK, USA).The samples were coated with gold to reduce sample charging and enhance SEM images. The pore size and surface area (SBET) were determined using Brunauer–Emmett–Teller (BET) method. The point of zero-charge (pHPZC) of MPPs was determined according to the drift method32. To properly assess the pHpzc, a series of solutions with initial pH values (pHi) ranging from 2.0 to 12 was set up with NaCl as the background electrolyte. Upon adding the desired amount of MPPs to each solution, the conical flasks were sealed with parafilm, and the suspensions were shaken at 150 rpm for 2 days. The final pH value (pHf) of each solution was then recorded, and the change (ΔpH) versus pHi was plotted. XRD also tested for the MPPs.Proximate and ultimate analysisThe proximate analysis of PPs was conducted in accordance with ASTM standards. The ash content was determined after heating in a furnace at 550 °C for 4 h. The carbon, nitrogen, hydrogen, and oxygen elemental cmpositions of PPs were measured applyingASTM D3176 standard procedure and using an elemental analyzer Model EA 1108 (Carl Erba Instruments).Enzyme assayThe oxidation of ABTS as a substrate was utilized for determining the enzyme’s activity. ABTS is an appropriate substrate for measuring the activity of laccase because it can be oxidized by laccase to create cation-radicals (ABTS+) that can be measured by spectrophotometrically. At typical assay conditions, the amount of enzyme that can oxidize one µmol of ABTS per minute was used to define one unit of enzyme activity. As reported in the literature33, for the free enzyme, 125 μL of diluted enzyme solution (2.5 mg/mL) was combined with 375 μL of newly made 0.1 mM ABTS in buffer solution at pH 4 for 2 min at 35 ̊C. The activity of LMPPs was determined by mixing 0.06 g in 6 mL of Mcilvaine buffer (0.12 M) pH 4 containing 0.5 mM ABTS and shaking it at 150 rpm for 15 min at room temperature. After centrifuging at a speed of 8000 rpm, an absrbance measurement was taken from a sampl of a constant volume at regular intervals of three min. Spectrophotometric analysis of the color development was then performed at 420 nm using UV–vis (Shimadzu UV-2450, Tokyo, Japan) and applying ε = 3.6 × 104 M−1 cm−1. The activity of LMPPs (laccase modified pomegranate peels) is expressed as U/g. Equations (1) and (2) were used for calculating immobilized and free enzyme activities, respectively34.$$mathrm{Immobilized ,laccase ,activity ,U}/mathrm{g}=frac{Delta mathrm{ab} imes {mathrm{D}}_{
m{f}} imes {mathrm{R}}_{
m{v}}}{upepsilon imes {t imes mathrm{M}}_{
m{support}}}$$
(1)
$$mathrm{Free ,laccase ,activiy ,U}/mathrm{mL}= frac{Delta mathrm{ab} imes {mathrm{D}}_{
m{f}} imes {mathrm{R}}_{
m{v}}}{upepsilon imes mathrm{t} imes mathrm{v}}$$
(2)
where (Delta)ab is the absorbance, Df is the dilution factor, RV is the reaction volume (mL), (upepsilon) (3.6 × 104 M−1 cm−1) isthe molar extinction coefficient, t is the reaction time (in), v is laccase amount (mL) and Msupport is mass of the support on which laccase has immobilized (g).ImmobilizationTwo grams of MPPs were employed to immobilize the laccase enzyme in 20 mL of buffer solution (pH 4) containing 2.5 mg/mL of laccase. The cocktail was stirred for 6 h at 35 °C and 150 rpm in a 50 mL tarson tube (Polypropylene/Spinwin Conical-Bottom). The cocktail was then centrifuged for 5 min at 8000 rpm. The immobilization yield was determined by dividing the difference between the enzyme activity in the supernatant prior to and after immobilization by the enzyme activity in the supernatant prior to immobilization35. The MPPs were washed twice with a 5 mL buffer solution (pH 4) to remove the excess enzyme, and the residual enzyme activity was also evaluated. The final product marked as LMPPs was refrigerated for further examination.pH, temperature, laccase dose, and storage stabilityRegarding the pH stabilizatio, 100 μL of free laccase (2.5 mg/mL) and 20 mg of LMPPs wer added to separate tubes containing 4 mL of buffer solutions (pH range: 3 to 8) and mixed at 150 rpm at 35 °C for 6 h. The residual laccase activity of both unbound and bound samples was tested. For thermal stability, a protocol identical to that for pH stabilization was followed, with the exception that samples were held at varying temperatures (10–60 °C) for 6 h at a fixed pH of 4. The optimum laccase dosage was determined by adding various laccase concentrations (ranging from 0.5 to 3 mg/mL) to 20 mg of LMPPs in separate tubes containing 4 mL of buffer solution (pH 4) and incubating them for 6 h at 35 °C and 150 rpm. For storage stability, free and immobilized enzyme samples were kept for up to two months at 4 and 25 °C, respectively, and the residual activity was evaluated every week.Reusability testsLMPPs (100 mg) was mixed with 2 mL of buffer solution (pH 4) comprising 0.5 mM ABTS and kept for 10 min at 35 °C and 150 rpm The sample was centrifuged for 3 min at 8000 rpm, and the cncentration of transformed ABTS in the supernatant was determined. Six cycles of washing with Milli-Q water and decanting were performed on LMPPs.HPLC analysisThe concentration of pollutants was determined using high-performance liquid chromatography (HPLC) type Merck-Hitachi D-700036. With gradient elution, the HPLC column used was a Zorbax SB-Aq of 150 mm length and 4.6 mm in diameter, with 5 µm particle size (Agilent, Santa Clara, CA, USA). The volume of the injected sample was 10 µL. The mobile phase was composed of 0.1% trifluoroacetic acid in Milli-Q water as eluent A and methanol as eluent B. The gradient program comprises 0–1 min of 40% mobile phase B and 1–5 min of a gradient to 100% mobile phase B. This lasted for up to eight minutes. Following this, the gradient reverted to its original state. The flow rate was set at 1 mL/min. Under these conditions, the compounds’ calibrations were linear between 5 and 100 g/mL.Rmoval test and long-term performanceIn batch experiments usin Milli-Q water and secondary effluent from a wastewater treatment plant, the effectiveness of LMPPs for removing emerging contaminants from an aqueous solution was examined. Before processing the wastewater samples, they were filtered using Whatman cellulose filter paper (47 mm circle) and the pollutants were spiked in the samples. In the tests, 100 mg of LMPPs was added to 40 mL of a pollutant mixture (50 mg/L, from each) and mixed at 150 rpm at room temperature. Samples of 2 mL were collected every half an hour, and then a 24-h sample was collected. The purpose of this step was to determine when the system reach equilibrium. Consequently, the system attained equilibrium at 120 min after evaluating the whole measurements. Based on the initial and final aqueous phase concentrations, the removal efficiency was calculated. The LMPPs were cleaned with Milli-Q water and dried, and the cycle continues (every 120 min). The removalof pollutants by MPPs (without laccase) due to adsorption was lso examined to understand the contribution of physical removal and degradation. This was accomplished by adding 100 mg of MPPs to 40 mL of a pollutant mixture (50 mg/L) and mixing at 150 rpm at room temperature. Samples of 2 mL were withdrawn every 30 min for two hours.Enzyme kinetic, adsorption isotherms, kinetics, and thermodynamicsThe Michaelis–Menten kinetic parameters of free and immobilized laccase were measured with ABTS at different concentrations in buffer solutions under optimal conditions, and the estimated kinetic parameters (Km and vm) were determined using the equations below.$$mathrm{v}=frac{{mathrm{v}}_{m }[mathrm{S}]}{{mathrm{K}}_{m}+[mathrm{S}]}$$
(3)
Where v is the reaction velocity (mM/ min), vm is the maximum reaction velocity (mM/ min), [S] is the substrate concentration (mM), and Km is the Michaelis–Menten constant (mM). Table 1 shows the models used for studying the adsorption istherms, kinetics, and thermodynamics.Table 1 Adsorption isotherms, kineics, and thermodynamics.Full size tableQuality controlAll experiments were conducted in triplicate, and results are presented as mean and standard deviation. The data were evaluated using the Kolmogorov–Smirnov test and results with p < 0.05 were considered statistically significant. Blank samples were also used in each experiment.Complies with international, national and/or institutional guidelinesExperimental research and field studies on plants (either cultivated or wild), including the collection of plant material, comply with relevant institutional, national, and international guidelines and legislation. Experimental studies were carried out in accordance with relevant institutional, national or international guidelines or regulations.Results and discussionMPPs characterizationFigure 1 depicts SEM images and EDS elemental maps for MPPs and LMPPs. There were no discernible surface texture alterations followig the immobilization of laccase. Due to their diminutive size (60–90 KDa, which corresponds to a particle size of less than 5 nm, laccases may not be identifiable by SEM at these magnifications. Micrographs with a 1 μm magnification have difficulty capturing this dimension42. Meanwhile, after the immobilization, the surface of LMPPs appeared smoother, most likely as a result of the laccase coating on the activated carbon surface43. Enzyme immobilization in magnetic biochar nanoparticles has been correlated with the smoothness of the surface44. Similar findings were observed in SEM images described in other investigations34,36,45. Activated MPPs with inorganic acids exhibited a more heterogeneous surface with deeper pores, which could be ascribed to the acid’s ability to remove impurities from the pores34. In a similar study, Lonappan and colleagues46 found that biochar subjected to citric acid exhibited more porous structures. The MPPs and LMPPs surfaces contain C, O, S, N, and Cl, asshown in Fig. 1. The presence of oxygen-containing groups on the surface as indicated by the presence of oxygen in MPPs and LMPPs EDS mapping. Element (N) increased in LMPPs relative to MPPs (Fig. S1), indicating the presence of laccase on the surface of the adsorbent34,36. However, the decrease in S concentration suggests that chemical reactions might have occurred during the treatment. Figure S2 depicts the XRD patterns of MPPs. A broad band between 20° and 30° corresponds to amorphous carbon. This also indicates that synthesized MPPs has more amorphous pore walls, a larger superficial area, and low crystallinity, presumably as a consequence of the high-temperature carbon pyrolysis.Figure 1SEM and EDS for MPPs and LMPPs. EDS scale is 1 µm.Full size imageThe FTIR spectra of the adsorbents are shown in Fig. 2. PPs, MPPs, and LMPPs exhibited CH2 stretching bands at 2922 and 2846 cm−1 that were asymmetrical and symmetrical, respectively. PPs, MPPs, and LMPPs contained a carbonyl phenoli groups indicated by the peak at 1632 cm−1 and at 1118 cm−1 bands, respectvely. MPPs and LMPPs exhibited C-O stretching at 1382 cm−1 as a result of chemical treatment by inorganic acids47. The presence of enzyme had a very subtle impact on the FTIR spectra of modified adsorbents as demonstrated by a slight increase and broadening of the peak at 3436 cm−1. This peak corresponds to laccase O–H and N–H bonds overlapping. Peak at 1632 cm−1 is expected to be associated with N–H stretching vibration and the amide bond existing in the laccase protein, which is regarded as an indicator of laccase protein content48.Figure 2FTIR spectra for PPs, MPPs and LMPPs.Full size imageThe formation of functional groups on the surface of carbonaceous substances offers optimal anchoring sites for the physical attachment and covalent bonding of enzymes to their surface49. Because carboxylic groups are easily produced through oxidizing treatment, they can undergo a variety of chemical reactions50. Additionaly, it has been reported that the presence of carboxyl groups on the surfaceof a carrier can enhance the immobilization of enzymes51. Thus, according to the results of the Boehm titration (Table 2), MPPs has a total acidity of 7.02 meq/g and are composed of carboxylic (1.27 meq/g), carbonyl (2.31 meq/g), and phenolic (3.44 meq/g) groups. The surface functional groups increased about 2.6-fold for the acidic groups and decreased by 0.08 meq/g for the total surface basicity. This increase was expected as during the activation process more acidic materials formed from the interaction between inorganic acids and the carbon precursor. The quantification of functional groups with Boehm titration agrees well with the qualitative FTIR results. These findings are in line with Zhang et al.52 who found a similar trend after activation with an increased acidic group and a decrease in the basic one. Another study used sonication in a mixture of H2SO4 and HNO3 acids, to modify single-walled carbon naotubes. It was discovered that 14 h of sonication contributed to cut nanotubs and increasing the concentration of COOH groups from 0.91 to 6.4 mmol/g53.Table 2 Boehm titration (meq/g).Full size tableSpecific surface area (SBET) and total pore volume (Vtotal) of PPs, MPPs, LMPPs were 47.6 m2/g and 0.163 cm3/g, 1249.1 m2/g and 0.831 cm3/g, 232.7 m2/g and 0.271 cm3/g, respectively, as shown in Table 3. Comparing the SBET from Table 3, it can be revealed that the SBET for PPs increased around 26.24 times after the modification. However, SBET for MPPs decreased by 81.40% after the immobilization step to become 232.7 m2/g for LMPPs. This larger reduction in the surface area provided quantitative proof for the immobilization of laccase via surface adsorption. These obtained surface area and pore volume in this study are in the same range as those reported in the literature. For instance, Hadi and colleagues54 prepared magnetized activated carbon synthesized from pomegranate husk and reportedVtot and SBET of 0.75 cm3/g and 1363.4 m2/g, respectively. Similarly, Taheri nd co-workers55 obtained Vtot and SBET of 0.83 cm3/g and 1576 m2/g, respectively, for their activated biochar made of the same raw materials but different activation methods using zinc chloride followed by hydrochloric acid treatment. Another study used microwave-induced and KOH-activation procedures for preparing pomegranate peel activated carbon and their measured SBET and Vtot were 941.02 m2/g and 0.470 cm3/g, respectively56. The SBET reduction following enzyme immobilization was also reported in numerous previous works. For instance, He and co-workers (2006)57 conducted an investigation to immobilize lipase on mesoporous silica which revealed a surface area reduction of up to 89.1%. Badgujar and colleagues58 tested immobilized lipase on a polymeric composite and found that the N-accessible surface decreased by 45%, from 0.804 to 0.437 m2/g. Similarly, Pirozzi and collaborators59 entrapped lipase in a ZrO2porous structure and reported that the support’s surface area decreased by 31% from 316 to 229 m2/g.Table 3 SBET, total pore volume, micropore volume, and mesopore volume of PPs, MPPs, LMPPs.Full size tableFigure 3 depicts the impact of different MPPs dosage on the pHpzc. The pHpzc was determined using the drift method, owing to its simplicity and inexpensive cost. The pHpzc was obtained from the intersection of the pH (pHfinal − pHinitial) and pHinitial. According to Fig. 3, the pHpzc values of MPPs at doses of 0.1, 0.2, and 0.4 g/L adsorbent were 5.9, 5.4, and 6.1, respectively. The pHpzc indicates that the MPPs has a positive surface charge at pH values less than 5.8 (the average value for three doses), demonstrating that acidic groups predominate on the surface of the MPPs and a negative surface charge at pH values greater than 5.8. In general, increased dosing of adsorbent caused the pH to drift toward point of zero charge (PZC)32, and thus the value of the PZC is dependent on th solid/liquid ratio. The different pHpzc values have been also reported in the cientific literature. For instance, Umpierres and co-workers60 investigated microwave applications for carbon-based adsorbents derived from Astrocaryum aculeatum seed and observed that the pHpzc value ranged between 4.44 and 6.71. Lima and colleagues61 observed that the pHpzc value for carbon-based compounds synthesized from Brazilian nutshells ranged from 5.86 to 6.31. This variation in pHpzc values is probably related to the raw biomass, activation and preparation methods for activated carbon.Figure 3pHpzc of different MPPs dosages.Full size imageThe physical and chemical properties of PPs are shown in Table 4. PPs consist of carbon (46.23%), oxygen (42.83%), hydrogen (5.43%), nitrogen (3.47%), and sulfur (2.03%). These compositions are comparable to other PPs structure reported in the literature. For instance, Ben-Ali and co-workers25 found that the PPs composition is carbon (43.13%), oxygen (48.15%), hyrogen (7.17%), nitrogen (0.66%), and sulfur (0.89%). Siddiqui et al.62 also repoted that the PPs main three elements were carbon (44.5%), oxygen (37.8%), and hydrogen (5.28%).Table 4 PPs physical properties and elemental composition.Full size tableOptimization of laccase immobilization parametersTo achieve optimal enzyme immobilization, the conditions were optimized by varying pH, temperature, and enzyme concentration. The pH of the solution influences the stability of the laccase, thus, rendering it an essential variable in the immobilization procedure. Figure 4A presents the tested pH range (2 to 8) on the LMPPs. At pH 2, laccase immobilization was lower owing to a loss of enzyme activity (10.34 U/g), whereas, at pH 4, optimal enzyme immobilization was obtained (49.54 U/g). With increasing pH more than 4, laccase immobilization on MPPs dropped sharply. At a pH less than the isoelectric point of 5.8 (the average value), the net charge on MPPs is positive, which improves the electrosttic attraction between the carrier and the negatively charged laccase63. Temperatre is also an essential variable in laccase immobilization, as enzymes are susceptible to heat by nature and are only functioning within specific temperature intervals. Figure 4B illustrates the temperature on the immobilization in the range of 10–60 °C. Laccase immobilization increased from 27.29 to 59.89 U/g as the temperature raised from 10 to 35 °C, which could be attributed to the higher rate of enzyme adsorption on MPPs. Following the optimum immobilization temperature (35 °C), the laccase immobilization decreased to 16.4 U/g at 60 °C as a result of a possible decrease in enzyme viability as the temperature increased64. Laccase concentration is vital for enzyme immobilization on MPPs. As shown in Fig. 4C, raising the enzyme concentration from 0.5 to 0.5 mg/mL enhanced enzyme immobilization from 21.40 to 68.76 U/g. Nevertheless, an additional increase in laccase concentration had no discernible effec on the immobilization of the laccase. This could be ascribed to the enzyme’s abilty to occupy available sites on the surface of MPPs. Enzyme immobilization on any material is contingent upon both the surface characteristics of the carrier and the immobilization settings. On the basis of a single-variable technique, the optimal immobilization settings were determined to be pH 4, a temperature of 35 °C, and an enzyme concentration of 2.5 mg/mL, which led to an immobilization yield of 69.8% (Fig. 4D). Increased immobilization yield was attributable to the optimal setting and modification of PPs with abundant carbonyl groups42. A lignocellulosic biochar immobilization yields of 64.23% has also been reported65.Figure 4The influence of varying pH (A), temperatures (B), and laccase concentrations (C) on the immobilization and yield (D).Full size imageLaccase stabilityThe pH of the solution may alter the ionization state of the amino acids in the enzyme, consequently affecting its structure,activity, and possibly leading to its denaturation66. Thus, the activity characteritics of free and immobilized laccase on MPPs were examined using activity assays at a range of pH values, as depicted in Fig. 5. Both free and immobilized laccase exhibited the highest levels of activity at pH 5 and 4, most likely due to the limited mobility of laccase caused by ionic interactions between the enzyme and MPPs67,68. In addition, LMPPs had a wider range of operating pH values than the free laccase, indicating that the LMPPs was more efficient than the free laccase under a variety of pH settings. The effect of temperature on the activity profiles of LMPPs and free laccase was also explored. According to Fig. 5, free laccase exhibited the highest enzyme activity at 30 °C, whereas immobilized laccase exhibited the maximum activity at 35 °C. Even at higher temperatures of 50 °C, 55 °C, and 60 °C, the LMPPs were more efficient than free laccase, with relative enzyme activities of 64.7%, 50.5%, nd 30.4%, respectively. The high activities of LMPPs shown in these high temperature could be because of the multipoint attachment between the laccase molecules and the MPPs, as well as the improved substrate diffusion capability at higher temperatures42. This also demonstrated that MPPs can assist in maintaining the activity of laccase, most likely because they could protect the conformational structure of laccase under various environmental circumstances69.Figure 5Stability of free and immobilized enzymes with regard to (A) pH and (B) temperature.Full size imageStorage stability and operational cyclesThe storage stability of immobilized laccase is a crucial determinant of its applications in industry such as wastewater treatment. The storage stability of free and immobilized laccase with two different temperatures (4 °C and 25 °C) was compared over two months as illustrated in Fig. 6 with error bars presented as bands. After one month, immobilized laccase retained approximately 92.7 and 86.3% of its initial activity at 25 °C and 4 °C, respectively. In addition, afte two months of storage, over 85.3% and 64.8% of the LMPPs initial activity were retained, at 25 °C and 4 °C, respectively. Comparatively, laccase retained approximately 75.5% and 72.7% of its catalytic properties after one months of storage at 25 °C and 4 °C, respectively. Upon completing 2 months of incubation at 25 °C and 4 °C, the free laccase activity decreased dramatically to 51.3% and 46.9% of its initial activities, respectively. The immobilized laccase is significantly more stable during storage, in contrast to the free one. This could be due to the stabilizing impact of the laccase’s three-dimensional structure after immobilization and the protective role of the carrier, which restricts conformational changes of the biocatalyst70.Figure 6Stability of free and immobilized laccase (LMPPs) with two different temperatures 4 °C and 25 °C.Full size imageAmong the benefits of immobilized enzyme is is reusability, which can also result in decreased costs and permit its application in ontinuous bioreactor operations71. To determine reusability, seven cycles of reaction between immobilized laccase and ABTS were examined for operational stability (Fig. 7). After seven cycles, immobilized laccase had lost approximately 48.2% of its initial activity. Since more than half of the initial laccase activity was still present after seven cycles of catalysis, laccase bound on MPPs appears to be reasonably stable. However, the following factors presumably led to the decline in activity: (1) a portion of immobilized laccase with weak binding was desorbed from the LMPPs during the rinsing procedure. Thus, only the laccase that is more firmly attached to the carrier is retained for subsequent cycles. (2) enzyme activity may be diminished throughout storage71. In this investigation, the operational stability experiment took a week to be completed, because the reaction between immobilized laccase nd ABTS was a slow process and consistently decreased as the measurements were performe. This was also reported in another study that measured the operational cycles for immobilized laccase on different types of wood biochar65. Cristóvão and colleagues35 immobilized laccase on green coconut fibers and found that after five cycles of ABTS oxidation, their biocatalyst lost 30% of its initial activity. Overall, it is obvious from reusability experiments that laccase immobilization on MPPs substantially improves the operational stability of the enzyme.Figure 7Stability results of immobilized laccase over seven operational cycles.Full size imageLaccase kineticsThe Michaelis constant (Km) is an essential factor for determining the affinity of laccase with its substrate, whereas the Vmax value indicates the maximal reaction velocity. A lower Km value indicates that the substrate has a higher binding affinity. The effect of substrate concentration (ABTS) between 0.05 and 2.0 mM on laccase immbilized activity at pH 4 was examined (Fig. 8). According to the Michaelis–Menten hyperblic trend, a rise in substrate concentration results in a rise in the enzymatic reaction rate. The findings demonstrated that the immobilized laccase had a lower Km value (0.21 mM) than the free laccase (0.56 mM), demonstrating the highest affinity towards ABTS and that the immobilization procedure could potentially have a positive effect on the substrate-enzyme interaction. This could be due to mass transfer limitations between the substrate and the surface of LMPPs. The lower Vmax value of immobilized laccase (3.68 mM/min) compared to that of free laccase (8.82 mM/min) could be a result of the immobilized laccase’s reduced flexibility and fewer accessible active sites. Other investigations have achieved a similar outcome72 demonstrating a decreased substrate affinity due to diffusional limitations and decreased enzyme flexibility after immobilization.Figure 8Michaelis–Menten fitting model for LMPs and free enzyme.Full size imageAdsorption isotherms and kineticsThe results of applyingexperimental data to the Langmuir and Freundlich isotherm models are depicted in Fig. 9. Langmuir isotherm model suits the compounds’ adsorption data better than the Freundlich model with correlation coefficients varying from 0.992 (amoxicillin and diclofenac) to 0.996 (ciprofloxacin). This suggests that the pharmaceutical molecules might have formed a monolayer on the surface of MPPs. The sorption capacity (qm) was calculated between 598.80 and 704.22 mg/g for ciprofloxacin and amoxicillin, respectively. As shown in Table 5 which illustrates Langmuir, Freundlich, Pseudo-1st-Order Model, and Pseudo-2nd-Order Model parameters, the separation factor (RL) values of the compounds between 0 and 1 indicates favorable adsorption. The Freundlich constant (n) is another factor applied in the adsorption literature to examine the favorability of the process. When the value of n is less than one, the adsorptin is deemed preferable73. The heterogeneity factor (1 ) is used as an indicator for measurng the difference in the energy distribution of the adsorption sites. In this study, the 1 values for the compounds were close to 0.8 indicating a heterogenous adsorption of the treated pharmaceuticals. Figure 10 depicts the pseudo-first and second-order models for the adsorption of chemicals. The experimental correlation coefficients best suit the pseudo-first-order kinetic model, which ranged from 0.984 (carbamazepine) to 0.995 (amoxicillin and ciprofloxacin). This demonstrates that physisorption governs the compounds adsorption rate onto MPPs. Figure 11 depicts the thermodynamic parameters plot of the compounds on MPPs at various temperatures (283, 293, 303, and 313 K). Table 6 shows the thermodynamic parameters of the pharmaceuticals’ adsorption onto MPPs. The Go values reduced as temperature increased, indicating that temperature has a positive effect on the effectiveness of adsorption. Negtive Go values determined at four temperatures demonstrate that the compounds spontaneouslyadsorb onto MPPs. The calculated H° values were positive, suggesting that the adsorption was endothermic. Finally, positive S° values implies that the adsorption process is stable and random74,75,76,77,78.Figure 9Langmuir (A) and Freundlich (B) isotherm models fittings.Full size imageTable 5 the parameter of Langmuir, Freundlich, Pseudo-1st-Order Model and Pseudo-2nd-Order Model.Full size tableFigure 10Adsorption kinetics of pharmaceuticals (A) pseudo-first-order and (B) pseudo-second-order.Full size imageFigure 11lnKl vs 1/T for MPPs.Full size imageTable 6 Thermodynamic parameters of emerging pollutants adsorption on MPPs.Full size tableTable S1 shows the residual sum of square (or error sum of square, SSE) for the isotherm and kinetic models. A low SSE demonstrates that the model fits the data which in this work followed the Langmuir model and pseudo-first-order.Emerging pollutants removal fro water and wastewater in short and long-term testsThis study assessed the biodegradation of moxicillin, ciprofloxacin, carbamazepine, and diclofenac in water and wastewater samples. Table S2 shows the secondary wastewater effluent characteristics. The adsorption of the target pollutants onto MPPs was examined through controlled experiments. The effectiveness of removing amoxicillin, ciprofloxacin, carbamazepine, and diclofenac from water and wastewater using LMPPs and MPPs over a two-hour period is depicted in Fig. 12. The letter A represents removal by adsorption only, whereas the letter L implies removal by adsorption and enzymatic degradation.Figure 12Emerging pollutants removal (%) with by LMPPs represented by a letter (L) and MPPs represented by (A), SD > 3.54%.Full size imageIn both water and wastewater, LMPPs performed better than MPPs. Within 1.5 h, the removal efficiencies for LMPPs and MPPs ranged from 86.8% (ciprofloxacin) to 90.4% (carbamazepine) and from 37.2% (ciproflxacin) to 46.3% (amoxicillin), respectively in water. After two hours, the emerging pollutantwas nearly completely removed with LMPPs, whereas MPPs removed approximately 70–75% of amoxicillin, carbamazepine, and diclofenac and 49.6% of ciprofloxacin. In wastewater samples, a percentage between 67.3% (ciprofloxacin) and 86.3% (diclofenac) was achieved in 1.5 h using LMPPs, and nearly a complete removal was obtained within 2 h. However, MPPs demonstrated a removal rate ranging from 29.8% (ciprofloxacin) to 53.2% (diclofenac) after 1.5 h treatment. In two hours, a removal range of 69.8–73.5% was attained for amoxicillin, carbamazepine, and diclofenac, and 46.3% for ciprofloxacin. Two hypothesized elimination processes could explain the superiority of LMPPs. It is expected that adsorption of pollutants onto the free sites occur first, followed by degradation of pollutants by laccases. The specific mechanisms likely involve common adsorption interactions such as covalent bonding (chemisorpion), hydrogen bonding and π–π (physical adsorption)79. Laccase residing within the porous strcture of MPPs then degrades the adsorbed pollutants. Functional groups perform an essential function in the degradation process as they get converted to free radicals, which can initiate domino reactions80.This system demonstrates its viability as a successful removal technique. However, its stability requires further investigation. Thus, the performance of system was gauged over six cycles of operation. Figure 13 demonstrates the system removal efficacy for six tested cycles. In all cycles, LMPPs had a better removal performance than MPPs for both water and wastewater samples. The removal of all pollutants declines as the number of cycles increases. The removal of the pollutants from wastewater lasted for five cycles while it continued up to six cycles with water. In water samples, the LMPPs can still remove the selected pollutants after six cycles with removal percentages ranging from 11.6%(ciprofloxacin) to 47.9% (amoxicillin). Consequently, using the adsorption process (MPPs) in th water medium, the system was able to perform 5 cycles with removal efficiencies ranging from 13.1% (ciprofloxacin) to 47.5% (amoxicillin). The removed pollutants by LMPPs in wastewater were better than MPPs with a removal efficiency in the 5th cycle ranging between 15.4% (ciprofloxacin) to 31% (diclofenac) for LMPPs and from 1.3% (carbamazepine) to 21.3% (diclofenac). Figure 14 depicts the proposed pharmaceutical degradation and removal using LMPPs. The decrease of catalytic effectiveness during subsequent cycles in both water and wastewater could be attributable to the occupation of adsorption sites, the scavenging of enzyme activities by other pollutants (in the case of wastewater) and the inactivation of the laccase. Additionally, the gradual reduction in the effectiveness of removal could be explained by leaching and denaturation of the laccase, as observed for ABTS oxidation29,81.Figur 13The removal efficiency of the emerging pollutants by LMPPs for water (A) and wastewater (B) oer sequential cycles. The standard deviations were between 2.65 and 5.43% for MPPs and LMPPs cycles.Full size imageFigure 14Schematic representation of degradation and removal of pharmaceuticals mechanism by LMPPs.Full size imageIt can be concluded that immobilized laccase onto adsorbents can actively be degraded and simultaneously remove pharmaceuticals even from treated wastewater. Nevertheless, the economics of the entire process requires further research. Testing the capacity of this technology for the removal of a wider variety of pollutants is also essential to prove its feasibility for removing emerging pollutants.ConclusionThis study examined the effectiveness of activated carbon prepared from pomegranate peels as an adsorbent and laccase enzyme carrier for removing emerging pollutants such as amoxicillin, carbamazepine, ciprofloxacin, and diclofenac. The temperature of 35 °C, pH of4, and laccase concentration of 2.5 mg/mL were determined to be the most effective immobilizationparameters for achieving a 69.8% immobilization yield. Emerging pollutant adsorption onto MPPs can be characterized as an endothermic spontaneous first-order reaction following the Langmuir isotherm. LMPPs performed better than MPPs at removing pollutants in both water and wastewater samples. Long-term tests demonstrated that LMPPs was superior to MPPs in removing the target compounds from water and wastewater effluent samples. Furthermore, this study demonstrated that activated carbon derived from pomegranate peels can be utilized as a carrier for setting up adsorption-enzymatic systems for eliminating emerging pollutants while maintaining a reasonable level of stability and reusability. In addition, recycling/reusing PPs might be perceived as a low carbon innovation option and fossil free activated carbon. Nevertheless, additional research needs to be conducted to determine the techniques efficacy with a more complex sample matrix. Issues of particular interest include the competitio between emerging contaminants and others for adsorption sites and their interaction with enzymes. Finally, system design parameters for a continuous large-scale process need to be investigated.
Data availability
All data generated or analysed during this study are included in this published article and its supplementary information files.
ReferencesRingler, C. et al. Global linkages among energy, food and water: An economic assessment. J. Environ. Stud. Sci. 6, 161–171 (2016).Article
Google Scholar
UNEP, United Nations Environment Programme and United Nations Human Settlements Programme. Sick Water: The Central Role of Wastewater Management in Sustainable Development—A Rapid Response Assessment. https://wedocs.unep.org/20.500.11822/9156 Accessed 13 Mar 2023 (2010)Büttner, O., Jawitz, J. W., Birk, S. & Borchardt, D. Why wastewaer treatment fails to protect stream ecosystems in Europe. Water Res. 217, 118382 (2022).Article
PubMed
Google Scholr
Grmasha, R. A. et al. Ecological and human health risk assessment of polycyclic aromatic hydrocarbons (PAH) in Tigris river near the oil refineries in Iraq. Environ. Res. 227, 115791 (2023).Article
CAS
PubMed
Google Scholar
Sauvé, S. & Desrosiers, M. A review of what is an emerging contaminant. Chem. Cent. J. 8, 1–7 (2014).Article
Google Scholar
Rathi, B. S., Kumar, P. S. & Show, P. L. A review on effective removal of emerging contaminants from aquatic systems: Current trends and scope for further research. J. Hazard. Mater. 409, 124413 (2021).Article
CAS
PubMed
Google Scholar
Wiest, L. et al. Occurrence and removal of emerging pollutants in urban sewage treatment plants using LC-QToF-MS suspect screening and quantification. Sci. Total Environ. 774, 145779 (2021).Article ADS
CAS
Google Scholar
Saleh, T. A., Baig, N., Othman, H. A. & Al Harith, A. M. Removal of alkanes by novel grassy cabbage microbuds prepare by an electrochemical method. Chem. Eng. J. 407, 126216 (2021).Article
CAS
Google Scholar
Baig, N., Alghunaimi, F. I., Dossary, H. S. & Saleh, T. A. Superhydrophobic and superoleophilic carbon nanofiber grafted polyurethane for oil–water separation. Process Saf. Environ. Prot. 123, 327–334 (2019).Article
CAS
Google Scholar
Al-Sareji, O. J. et al. Ketoprofen and aspirin removal by laccase immobilized on date stones. Chemosphere 311, 137133 (2023).Article
ADS
CAS
Google Scholar
Bilal, M., Adeel, M., Rasheed, T., Zhao, Y. & Iqbal, H. M. Emerging contaminants of high concern and their enzyme-assisted biodegradation—A review. Environ. Int. 124, 336–353 (2019).Article
CAS
PubMed
Google Scholar
Cha, J. Y. et al. Fungal laccas-catalyzed oxidation of naturally occurring phenols for enhanced germination and salt tolerance of Arabidopsis thaliana: A green route for synthesizing humic-like fertilizers. J. Agric. Food Chem. 65(6, 1167–1177 (2017).Article
CAS
PubMed
Google Scholar
Ji, C., Hou, J. & Chen, V. Cross-linked carbon nanotubes-based biocatalytic membranes for micro-pollutants degradation: Performance, stability, and regeneration. J. Membr. Sci. 520, 869–880 (2016).Article
CAS
Google Scholar
Xenopoulos, A. A new, integrated, continuous purification process template for monoclonal antibodies: Process modeling and cost of goods studies. J. Biotechnol. 213, 42–53 (2015).Article
CAS
PubMed
Google Scholar
Majeau, J. A., Brar, S. K. & Tyagi, R. D. Laccases for removal of recalcitrant and emerging pollutants. Biores. Technol. 101(7), 2331–2350 (2010).Article
CAS
Google Scholar
Ba, S., Arsenault, A., Hassani, T, Jones, J. P. & Cabana, H. Laccase immobilization and insolubilization: from fundamentals to applications for the elimination of emerging contaminants in wastewater treatment. Crit. Rev. Biotechnol. 33(4), 404–418 (2013).Article CAS
PubMed
Google Scholar
Girelli, A. M., Astolfi, M. L. & Scuto, F. R. Agro-industrial wastes as potential carriers for enzyme immobilization: A review. Chemosphere 244, 125368 (2020).Article
ADS
CAS
PubMed
Google Scholar
Bijoy, G., Rajeev, R., Benny, L., Jose, S. & Varghese, A. Enzyme immobilization on biomass-derived carbon materials as a sustainable approach towards environmental applications. Chemosphere 4, 135759 (2022).Article
ADS
Google Scholar
Kahramanoglu, I. Trends in pomegranate sector: Production, postharvest handling and marketing. Int. J. Agric. For. Life Sci. 3(2), 239–246 (2019).
Google Scholar
Jalal, H. et al. Physico-chemical and functional roperties of pomegranate peel and seed powder. J. Pharm. Innov 7, 1127–1131 (2018).
Google Scholar
Akram, M. et al. Highly efficient removal of phosphate from aqueous media by pomegranate peel co-doping with ferric chloride and lanthanum hydroxide nanoparticle. J. Clean. Prod. 292, 125311 (2021).Article
CAS
Google Scholar
Abedi, M., Salmani, M. H. & Mozaffari, S. A. Adsorption of Cd ions from aqueous solutions by iron modified pomegranate peel carbons: Kinetic and thermodynamic studies. Int. J. Environ. Sci. Technol. 13, 2045–2056 (2016).Article
Google Scholar
Oymak, T. & Şafak, E. S. Removal of sulfadiazine from aqueous solution by magnetic biochar prepared with pomegranate peel. Sep. Sci. Technol. 57(16), 2521–2531 (2022).Article
CAS
Google Scholar
Bouallegue, M. C., Trifi, B., Marzouk Trifi, I., Zahraa, O. & Alatrache, A. Removal of an emerging pharmaceutical pollutant, sulfasalazine, by adsortion onto pomegranate peels. Chem. Eng. Commun. 209(7), 957–966 (2022).Article
CAS
Google Scholar
Ben-Ali, S., Jaouali, I., Souissi-Najar, S. & Ouederni, A. Characterization and adsorption capacity of raw pomegranate peel biosorbent for copper removal. J. Clean. Prod. 142, 3809–382 (2017).Article
CAS
Google Scholar
Zhang, Y., Geißen, S. U. & Gal, C. Carbamazepine and diclofenac: Removal in wastewater treatment plants and occurrence in water bodies. Chemosphere 73(8), 1151–1161 (2008).Article
ADS
CAS
PubMed
Google Scholar
Loos, R., Marinov, D., Sanseverino, I., Napierska, D. & Lettieri, T. Review of the 1st Watch List Under the Water Framework Directive and Recommendations for the 2nd Watch List, EUR 29173 EN (Publications Office of the European Union, 2018) (978-92-79-81838-7 (print),978-92-79-81839-4 (pdf), doi:10.2760/614367 (online),10.2760/701879 (print), JRC111198).
Google Scholar
Nghdi, M. et al. Pinewood nanobiochar: A unique carrier for the immobilization of crude laccase by covalent bonding. Int. J. Biol. Macromol. 115, 563–571 (2018).Article
CAS
PubMed
Google Scholar
Naghdi, M. et al. Immobilized laccase on oxygen functionalized nanobiochars through mineral acids treatment for removal ofcarbamazepine. Sci. Total Environ. 584, 393–401 (2017).Article
ADS
PubMed
Google Scholar
Boehm, H. P. Surface oxides on carbon and their analysis: A critical assessment. Carbon 40(2), 145–149 (2002).Article
CAS
Google Scholar
Goertzen, S. L., Thériault, K. D., Oickle, A. M., Tarasuk, A. C. & Andreas, H. A. Standardization of the Boehm titration. Part I. CO2 expulsion and endpoint determination. Carbon 48(4), 1252–1261 (2010).Article
CAS
Google Scholar
Kosmulski, M. Surface Charging and Points of Zero Charge (CRC Press, 2009).Book
Google Scholar
Suman, S. K., Ptnam, P. L., Ghosh, S. & Jain, S. L. Chicken feather derived novel support material for immobilization of laccase and its application in oxidation of veratryl alcohol. ACS Sustain. Chem. Eng. 7(3), 3464–3474 (2018).Article
Google Scholar
Pandey, D., Daverey, A., Dutta, K. & Arunachalam, K. Bioremoval of toxic malachite green from water through simultaneus decolorization and degradation using laccase immobilized biochar. Chemosphere 297, 134126 (2022).Article
ADS
CAS
PubMed
Google Scholar
Cristóvão, R. O. et al. Immobilization of commercial laccase onto green coconut fiber by adsorption and its application for reactive textile dyes degradation. J. Mol. Catal. B Enzyme 72(1–2), 6–12 (2011).Article
Google Scholar
Al-sareji, O. J. et al. Removal of emerging pollutants from water using enzyme-immobilized activated carbon from coconut shell. J. Environ. Chem. Eng. 14, 109803 (2023).Article
Google Scholar
Langmuir, I. The constitution and fundamental properties of solids and liquids. Part I. Solids. J. Am. Chem. Soc. 38(11), 2221–2295 (1916).Article
CAS
Google Scholar
Freundlich, H. M. F. Over the adsorption in solution. J. Phys. chem 57(385471), 1100–1107 (1906).
Google Scholar
Lagergren, S. Zur theorie der sogenannten adsorption geloster stoffe. Kungliga svenska vetenskapsakaemiens. Handlingar 24, 1–39 (1898).
Google Scholar
Srivastava, V. C., Mall, I. D. & Mishra, I. M. Adsorption of toxic metal ions onto activated carbon: Study of sorption behaviour through characterization and kinetics. Chem. Eng. Process. 47(8), 1269–1280 (2008).Article
Google Scholar
Singh, S. et al. Sustainable removal of Cr (VI) using graphene oxide-zinc oxide nanohybrid: Adsorption kinetics, isotherms and thermodynamics. Environ. Res. 203, 111891 (2022).Article
CAS
PubMed
Google Scholar
Lonappan, L. et al.Covalent immobilization of laccase on citric acid functionalized micro-biochars derived from different feedstock and removal of diclofenac. Chem. Eng. J. 351, 985–994 (2018).Article
CAS
Google Scholar
Zhang, Y. et al. Immobilization of laccase on magnetically separable biochar for highly efficient removal of bisphenol A in water. RSC Adv. 10(8), 4795–4804 (2020).Article
ADS
CAS
PubMed
PubMed Central
Google Scolar
He, L. et al. Multi-layered enzyme coating on highly conductive magnetic biochar nanoparticles for bisphenol A sensing in water. Chem. Eng. J. 384, 123276 (2020).Article
CAS
Google Scholar
Qiu, H. et al. Adsorption of laccase on the surface of nanoporous gold and the direct electron transfer between them. J. Phys. Chem. C 112(38), 14781–14785 (2008).Article
CAS
Google Scholar
Lonappan, L., Liu, Y., Rouissi, T., Brar, S. K. & Surampalli, R. Y. Development of biochar-based greenfunctional materials using organic acids for environmental applications. J. Clean. Prod. 244, 118841 (2020).Article
CAS
Google Scholar
Baig, N., Chauhan, D. S., Saleh, T. A. & Quraishi, M. A. Diethylenetriamine functionalized graphene oxide as a novel corrosion inhibitor for mild steel in hydrochloric acid solutions. New J. Chem. 43(5), 2328–2337 (2019).Article
CAS
Google Scholar
Hu, J., Yuan, B., Zhang, Y. & Guo, M. Immobilization of laccse on magnetic silica nanoparticles and its application in the oxidation of guaiacol, a phenolic lignin model compound. RSC Adv. 5(120), 99439–99447 (2015).Article
ADS
CAS
Google Scholar
Gao, Y. & Kyratzis, I. Covalent immobilization of proteins on carbon nanotubes using the cross-linker 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide—A critical assessment. Bioconjug. Chem. 19(10), 1945–1950 (2008).Article
CAS
PubMed
Google Scholar
Jiang, K. et al Protein immobilization on carbon nanotubes via a two-step process of diimide-activated amidation. J. Mater. Chem. 14(1), 37–39 (2004).Article
CAS
Google Scholar
Cho, Y. K. & Bailey, J. E. Immobilization of enzymes on activated carbon: Selection and preparation of the carbon support. Biotechnol. Bioeng. 21(3), 461–476 (1979).Article
CAS
PubMed
Google Scholar
Zhang, G. et al. Aerobic granular sludge-derived activated carbon: Mineral acid modification and superior dye adsorpion capacity. RSC Adv. 5(32), 25279–25286 (2015).Article
ADS
CAS
Google Scholar
Marshall, M. W., Popa-Nita, S. & Shapter, J. G. Measurement of functionalised carbon nanotube carboxylic acid groups using a simple chemical process. Carbon 44(7), 1137–1141 (2006).Article
CAS
Google Scholar
Hadi, S., Taheri, E., Amin, M. M., Fatehizadeh, A. & Khayet, M. Magnetized activated carbon synthesized from pomegranate husk fo persulfate activation and degradation of 4-chlorophenol from wastewater. Appl. Sci. 12(3), 1611 (2022).Article
CAS
Google Scholar
Taheri, E., Fatehizadeh, A., Lima, E. C. & Rezakazemi, M. High surface area acid-treated biochar from pomegranate husk for 2, 4-dichlorophenol adsorption from aqueous solution. Chemosphere 295, 133850 (2022).Article
ADS
CAS
PubMed
Google Scholar
Ahmad, M. A., Puad, N. A. A. & Bello, O. S. Kinetic, equilibrium and thermodynamic studies of synthetic dye removal using pomeranate peel activated carbon prepared by microwave-induced KOH activation. Water Resour. Ind. 6, 18–35 (2014).Article
Google Scholar
He, J., Song, Z., Ma, H., Yang, L. & Guo, C. Formation of a mesoporous bioreactor based on SBA-15 and porcine pancreatic lipase by chemical modification following the uptake of enzymes. J. Mater. Chem. 16(44), 4307–4315 (2006).Article
CAS
Google Scholar
Badgujr, K. C., Dhake, K. P. & Bhanage, B. M. Immobilization of Candida cylindracea lipase on poly lactic acid, polyvinyl alcohol and chitosan based ternary blend film: Characterization, activity, stability and its application for N-acylation reactions. Process Biochem. 48(9), 1335–1347 (2013).Article
CAS
Google Scholar
Pirozzi, D., Fanelli, E., Aronne, A., Pernice, P. & Mingione, A. Lipase entrapment in a zirconia matrix: Sol–gel synthesis and catalytic properties. J. Mol. Catal. B Enzym. 59(1–3), 116–120 (2009).Article
CAS
Google Scholar
Umierres, C. S. et al. Microwave-activated carbons from tucumã (Astrocaryum aculeatum) seed for efficient removal of 2-nitrophenol from aqueous solutions. Environ. Technol. 39(9), 1173–1187 (2018).Article
CAS
PubMed
Google Scholar
Lima, D. R. et al. Efficient acetaminophen removal from water and hospital effluents treatment by activated carbons derived from Brazil nutshells. Collids Surf. A 583, 123966 (2019).Article
CAS
Google Scholar
Siddiqui, M. T. H. et al. Characterization and process optimization of biochar produced using novel biomass, waste pomegranate peel: A response surface methodology approach. Waste Biomass Valoriz. 10, 521–532 (2019).Article
CAS
Google Scholar
Imam, A. et al. Application of laccase immobilized rice straw biochar for anthracene degradation. Environ. Pollut. 268, 115827 (2021).Article
CAS
PubMed
Google Scholar
Wang, Z. et al. The study of laccase immobilization optimization and stability improvemen on CTAB-KOH modified biochar. BMC Biotechnol. 21, 1–13 (2021).Article
Google Scholar
Li, N., Xia, Q., Niu, M., Ping, Q. & Xiao, H. Immobilizing laccase on different species wood biochar to remove the chlorinated biphenyl in wastewater. Sci. Rep. 8(1), 13947 (2018).Article
ADS
PubMed
PubMed Central
Google Scholar
Tahera, M. et al. Degradation of chlortetracycline using immobilized laccase on polyacrylonitrile-biochar composite nanofibrous membrane. Sci. Total Environ. 605, 315–321 (2017).Article
ADS
PubMed
Google Scholar
Alver, E. & Metin, A. Ü. Chitosan based metal-chelated copolymer nanoparticles: Laccase immobilization and phenol degradation studies. Int. Biodeterior. Biodegrad. 125, 235–242 (2017).Article
CAS
Google Scholar
Wang, F., Guo, C., Yang, L. R. & Liu, C. Z. Magnetic mesoporous silica nanoparticles: Fabrication and their laccase immobilization performance. Biores. Technol. 101(23), 8931–8935 (2010).Aticle
CAS
Google Scholar
Cea, M., González, M. E., Abarzúa, M. & Navia, R. Enzymatic esterification of oleic acid by Candida rugosa lipase immobilized onto biochar. J. Environ. Manag. 242, 171–177 (2019).Article
CAS
Google Scholar
Xu, R., Chi, C., Li, F. & Zhang, B. Laccase–polyacrylonirile nanofibrous membrane: Highly immobilized, stable, reusable, and efficacious for 2, 4, 6-trichlorophenol removal. ACS Appl. Mater. Interfaces 5(23), 12554–12560 (2013).Article
CAS
PubMed
Google Scholar
Celikbicak, O. et al. Immobilization of laccase on hairy polymer grafted zeolite particles: Degradation of a model dye and product analysis with MALDI–ToF–MS. Microporous Mesoporous Mater. 199, 57–65 (2014).Article
CAS
Google Scholar
Cabana, H., Alexandre, C., Agathos, S. N. & Jones, J. P. Immobilization of laccase from the white rot fungus Coriolopsis polyzona and use of the immobilized biocatalyst for the continuous elimination ofendocrine disrupting chemicals. Biores. Technol. 100(14), 3447–3458 (2009).Article
CAS
Google Scholar
Ghaedi, M., Mortazavi, K., Montazerozohori, M., Shokrollahi, A. & Soylak, M. Flame atomic absorption spectrometric (FAAS) determination of copper, iron and zinc in food samples ater solid-phase extraction on Schiff base-modified duolite XAD 761. Mater. Sci. Eng., C 33(4), 2338–2344 (2013).Article
CAS
Google Scholar
Yao, X. et al. Magnetic activated biochar nanocomposites derived from wakame and its application in methylene blue adsorption. Biores. Technol. 302, 122842 (2020).Article
CAS
Google Scholar
Singh, S., Kumar, V., Romero, R., Sharma, K. & Singh, J. Applications of nanoparticles in wastewater treatment. Nanobiotechnol. Bioformul. 34, 395–418 (2019).Article
Google Scholar
Narasimhappa, P., Varshney, R., Singh, S., Naik, T. S. K. & Ramamurthy, P. C. 3D rhombohedral microcrystals metal-organic frameworks for electrocemical and fluorescence sensing of tetracycline. Chemosphere 333, 138977 (2023).Article
ADS
CAS
PubMed
Google Scholar
Singh, S. et al. Mechanism and kinetics of Cr (VI) adsorption on biochar derived from Citrobacter freundii under different pyroysis temperatures. J. Water Process Eng. 47, 102723 (2022).Article
Google Scholar
Singh, S., Kapoor, D., Khasnabis, S., Singh, J. & Ramamurthy, P. C. Mechanism and kinetics of adsorption and removal of heavy metals from wastewater using nanomaterials. Environ. Chem. Lett. 19, 2351–2381 (2021).Article
CAS
Google Scholar
Singh, S. et al. Adsorption and detoxification of pharmaceutical compounds from wastewater using nanomaterials: A review on mechanism, kinetics, valorization and circular economy. J. Environ. Manag. 300, 113569 (2021).Article
CAS
Google Scholar
Arregui, L. et al. Laccases: Structure, function, and potential application in water bioremediation. Microb. Cell Fact. 18(1),1–33 (2019).Article
Google Scholar
Lloret, L. et al. Immobilization of laccase by encapsulation in a sol–gel matrix and its characterization and use for the removal of estrogens. Biotechnol. Prog. 27(6), 1570–1579 (2011).rticle
CAS
PubMed
Google Scholar
Ariaeenejad, S., Motamedi, E. & Salekdeh, G. H. Highly efficient removal of dyes from wastewater using nanocellulose from quinoa husk as a carrier for immobilization of laccase. Biores. Technol. 349, 126833 (2022).Article
CAS
Google Scholar
García-Delgado, C. et al. Degradation of tetracyclines and sulfonamides by stevensite-and biochar-immobilized laccase systems and impact on residual antibiotic activity. J. Chem. Technol. Biotechnol. 93(12), 3394–3409 (2018).Article
Google Scholar
Chen, X., Zhou, Q., Liu, F., Peng, Q. & Teng, P. Removal of nine pesticide residues from water and soil by biosorption coupled with degradation on biosorbent immobilized laccase. Chemosphere 233, 9–56 (2019).Article
ADS
CAS
PubMed
Google Scholar
da Silva, C. K. H. et al. Laccase covalently immobilized on avocado seed biochar: A high-performance biocatalyst for acetaminophe sorption and biotransformation. J. Environ. Chem. Eng. 10(3), 107731 (2022).Article
Google Scholar
Dos Santos, P. M. et al. Corn cob as a green support for laccase immobilization—Application on decolorization of Remazol Brilliant Blue R. Int. J. Mol. Sci. 23(16), 9363 (2022).Article
PubMed
PubMed Central
Google Scholar
Download referencesAcknowledgementsThe authors are appreciative of the warm work of the editor and the anonymous reviewers earnestly. The viewpoints or opinions presented in this manuscript are those of the authors. The ÚNKP-22-3-I-PE-12 (Osamah J. Al-sareji) New National Excellence Program of the Ministry for Culture and Innovation from the source of the National Research, Development and Innovation Fund supported this research.FundingOpen accessfunding provided by University of Pannonia. The ÚNKP-22-3-I-PE-12 (Osamah J. Al-sareji) New National Excellence Program of the Ministry for Culture and Innovation from the source of he National Research, Development and Innovation Fund supported this research.Author informationAuthors and AffiliationsSustainability Solutions Research Lab, Faculty of Engineering, University of Pannonia, Egyetem str. 10, Veszprém, 8200, HungaryOsamah J. Al-sareji, Mónika Meiczinger & Viola SomogyiEnvironmental Research and Studies Center, University of Babylon, Al-Hillah, Babylon, IraqOsamah J. Al-sareji & Ruqayah Ali GrmashaNYUAD Water Research Center, New York University-Abu Dhabi Campus, P.O. Box 129188, Abu Dhabi, United Arab EmiratesRaed A. Al-JubooriWater and Environmental Engineering Research Group, Department of Built Environment, Aalto University, Aalto, P.O. Box 15200, 00076, Espoo, FinlandRaed A. Al-JubooriResearch Group of Limnology, Faculty of Engineering, Center for Natural Science,University of Pannonia, Egyetem u. 10, Veszprém, 8200, HungaryRuqayah Ali Grmasha, Csilla Stenger-Kovács & Edina LengyelSchool of Civil Engineering and Built Environment, Liverpol John Moores University, Liverpool, UKManolia Andredaki, Ibijoke A. Idowu & Khalid S. HashimELKH-PE Limnoecology Research Group, Egyetem utca 10, Veszprém, 8200, HungaryCsilla Stenger-Kovács & Edina LengyelDepartment of Materials Sciences and Engineering, Research Centre of Engineering Sciences, University of Pannonia, P.O. Box 158, Veszprém, 8201, HungaryMiklós Jakab Department of Environmental Engineering, College of Engineering, University of Babylon, Al-Hillah, Babylon, IraqKhalid S. HashimAuthorsOsamah J. Al-sarejiView author publicationsYou can also search for this author in
PubMed Google ScholarMónika MeiczingerView author publicationsYou can also search for this author in
PubMed Google ScholarRaed A. Al-JubooriView author publicationsYou can also search for this author in
PubMedGoogle ScholarRuqayah Ali GrmashaView author publicationsYou can also search for this author in
PubMed Google ScholarManolia AndredakiView author publicationsYo can also search for this author in
PubMed Google ScholarViola SomogyiView author publicationsYou can also search for this author in
PubMed Google ScholarIbijoke A. IdowuView author publicationsYou can also search for this author in
PubMed Google ScholarCsilla Stenger-KovácsView author publicationsYou can also search for this author in
PubMed Google ScholarMiklós JakabView author publicationsYou can also search for this author in
PubMed Google ScholarEdina LengyelView author publicationsYou can also search for this author in
PubMed Google ScholarKhalid S. HashimView author publicationsYou can also search for this author in
PubMed Google ScholarContributionsO.J.A.: Formal analysis, Data curation, Visualization, Methodology, Investigation, Resources, Conceptualization, Funding acquisition, Software,Validation, Writing-original draft, Writing-re-view & editing.
M.M.: Supervision, Methodology, Resources, Writing-review & ediing.
R.A.A.: Writing-review & editing, Methodology, Investigation.
R.A.G.: Writing-review & editing, Methodology, Visualization, Software.
M.A.: Validation, Writing-review & editing.
V.S.: Supervision, Resources, Writing-review & editing.
I.A.I.: Validation, Writing-review & editing.
C.S.-K.: Methodology.
M.J.: Methodology.
E.L.: Methodology.
K.S.H.: Methodology, Validation, Writing-review & editing.Corresponding authorCorrespondence to
Osamah J. Al-sareji.Ethics declarations
Competing interests
The authors declare no competing interests.
Additional informationPublisher’s noteSpringer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.Supplementary InformationSupplementary Information.Rights and permissions
Open Access This article is licensed under a reative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution nd reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Reprints and PermissionsAbout this articleCite this articleAl-sareji, O.J., Meiczinger, M., Al-Juboori, R.A. et al. Efficient removal of pharmaceutical contaminants from water and wastewater usig immobilized laccase on activated carbon derived from pomegranate peels.
Sci Rep 13, 11933 (203). https://doi.org/10.1038/s41598-023-38821-3Download citationReceived: 01 May 2023Accepted: 15 July 2023Published: 24 July 2023DOI: https://doi.org/10.1038/s41598-023-38821-3Share this articleAnyone you share the following link with will be able to read this content:Get shareable linkSorry, a shareable link is not currently available for this article.Copy to clipboard
Provided by the Springer Nature SharedIt content-sharing initiative
CommentsBy submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.